H12 TOOLING RESIN FIBROLIT®-ZWO / FIBROFIX®-SECHS - PROPERTIES THINNING AGENT FOR FIBROLIT®-ZWO - PROPERTIES FIBROLIT®-MK METAL ADHESIVE - PROPERTIES Physical properties thinning agent for FIBROLIT®-ZWO: Density 1,16 ± 0,02 g/ml flash point (DIN 51584) 97 °C shelf life at 20 - 25 °C approx. 1 year viscosity at 25 °C 1000 ± 100 mPas Physical properties metal adhesive FIBROLIT®-MK: density of Resin MK 1,16 ± 0,01 g/ml density of Hardener MK 1,13 ± 0,01 g/ml tensile shear strength 40 - 50 N/mm2 thermal resistance (Martens) 45 - 50 °C pot life (100 g-mixture) 15 - 20 min shelf life at 20 - 25 °C approx. 1 year time for complete curing at 20 - 25 °C approx. 24 h Chemical resistance Chemical substance Assessment Acetone C Formaline 30% B Xylol A Silicone solution DC 20 A Diesel A White spirits C Tetrachloroethylene A Perchloroethylene A Ethyl acetate C Epichlorohydrene C Fluoric acid 10% C Chlophen T 64 A Water B Sea Water B NaCl solution of 5% A Formic acid C Lactic acid 10% C Sulphuric acid C Acetic acid 10% C Ammonia 25% B Aniline C Phenol-90 C Hydrochloric acid 10% B A = no effect B = minimal effect C = destructive effect Physical properties tooling resin FIBROLIT®-ZWO / FIBROFIX®-SECHS: viscosity at 25 °C approx. 9000 mPas pot life at 25 °C (mixed = 100 g) approx. 25 min. curing time at 20 - 25 °C* approx. 24 h shelf life at 20 - 25 °C approx. 1 year thermal resistance (Martens) DIN 53458 approx. 50 - 55 °C (75 - 80 °C*) flashpoint of resin approx. 210 °C flashpoint of hardener approx. 207 °C decomposition temperature (ISO/R 871-68) >300 °C Thermal conductivity, within range of 14-38 °C (VDE 0304 section 1/7.59) 0,531 W/km density (resin) approx. 2,5 g/ml density (hardener) approx. 1.06 g/ml compressive strength DIN EN ISO 604 approx. 130 - 140 N/mm2 tensile strength DIN EN ISO 527-1, -2, -3 approx. 50 N/mm2 flexural strength DIN EN ISO 178 approx. 70 N/mm2 ball indentation test DIN EN ISO 2039-1 approx. 213 N/mm2 impact test 3,57 KJ/m2 modulus of elasticity (ex tensile test) approx. 8760 N/mm2 linear shrinkage approx. 0.05 - 0.12 % *Cured at ambient room temperature for 24 hours, or 15 hours at 50 °C
RkJQdWJsaXNoZXIy MTIwNzY0